stainless steel 436 - coil slitting 436 UNS S43600 This variation of Type 430 is alloyed with
columbium and molybdenum to reduce the tendency
of wavy lines (roping) developing during forming,
improve buffing qualities, somewhat improve resistance
to cracking in limited forming operations and improve
corrosion resistance. Corrosion resistance is not
equal to the 300 series. This type is highly magnetic
with satisfactory abrasion resistance. Automotive
and appliance trims are typical applications.
chemical composition limits
(%)
Carbon
C
Manganese
Mn
Phosphorus
P
Sulfur
S
Silicon
Si
Chromium
Cr
Columbium
Cb
Molybdenum
Mo
0.12
1.00
0.040
0.030
1.00
16.00-18.00
5 x C min./0.70 max
0.75-1.25
Representative mechanical property
condition
tensile strength
yield strength
elongation
rockwell
KSi
MPa
ksi
mpa
in
2 inches %
Annealed
65
(450)
40
(273)
20
B-90
max.
*Minimum
Chemical composition is percent maximum unless
shown as a range or a minimum.
Information presented as a guide for reference
purposes only and is not intended for product
design or application.